Hydrocarbon synthesis



March 10, 1953 Q KElTH 2,631,159

HYDROCARBON SYNTHESIS Original Filed Jan. 51, 1945 v i /g l 9 INVENTOR.

\ P/SFC/I/AL 0. /77-/ w r BY Patented Mar. 10, 1953 HYDROCARBON SYNTHESIS Percival C. Keith, Peapack, N. J assignor to Hydrocarbon Research, Inc., New York, N. Y., a corporation of New Jersey Original application January 31, 1945, Serial No.

1949, Serial No. 96,520

7 Claims.

This application is a division of my copending application, Serial No. 575,417, filed January 31, 1945.

This invention relates to an improved process and means for conducting reactions between carbon monoxide and hydrogen; more particularly, the invention is directed to the production of liquid hydrocarbons by the hydrogenation of carbon monoxide in the presence of a fluidized mass of pulverulent catalyst.

As is widely reported in the technical literature, a major problem that has been encountered in the commercialization of the synthesis of hydrocarbons is that of removing heat and controlling temperature in a practical and effective manner. The catalytic hydrogenation of carbon monoxide is a strongly exothermic chemical reaction and it is extremely important to prevent any appreciable rise in the desired reaction temperature inasmuch as a temperature rise of as little as 10 F. or less may shift the reaction to the production of less valuable products, e. g., fixed hydrocarbon gases like methane and others. Such a rise in reaction temperature not only lowers the yield of the more valuable liquid products by promoting the formation of gaseous products, but also increases the rate of reaction so that a vicious circle of rising temperature is initiated. Obviously, the greater the temperature rise, the greater is the shift in product distribution in the direction of less valuable products.

While numerous schemes have been proposed to meet these exacting requirements of heat removal and temperature control, as far as I know, not one has been found which is entirely satis factory or free of some peculiar disadvantage.

A recent patent suggests flowing synthesis gases containing suspended therein the powdered catalyst through parallel tubular reaction zones without which a cooling medium is circulated to remove the heat of reaction. While this system is largely successful in the attainment of its prime objective, i. e., removal of the heat of reaction along the path of flow of the reaction gases, it has three serious handicaps from a commercial point of view. In the first place, for an adequate contact time between the synthesis gas and catalyst, the reactor must be of enormous volume and excessive height. The height is so great that the only practical way of erecting a plant of this type would be to use several reactors of reasonable height connected in series. Another shortcoming of this suggested process is the considerable attrition of the equipment and powdered catalyst which occurs at the high gas velocity required to carry the catalyst along in suspension. In addition, such a process necessitates cumbersome and expensive auxiliary Divided and this application June 1,

mic-449.6)

equipment, particularly separators of gases and solids which are subjected to heavy attritive service. These factors make for such high installation and maintenance costs that it is genuinely doubted that a plant of this type can be economically feasible.

Another recent patent proposes passing synthesis gas through a fluent but dense mass of particulate catalyst, absorbing the heat of conversion in the catalyst, moving the catalyst from the synthesis zone to an outside cooling zone and reintroducing the cooled catalyst for absorbing the heat of reaction in the synthesis zone. While this method has the distinct advantage over the preceding one of reducing the volume and, especially, the height of the reaction zone to reasonable magnitudes, it suffers from the limitation that the removal of heat is dependent on the low specific heat of the catalyst. This means that a relatively large mass of catalyst must be circulated at a high rate. Furthermore, inasmuch as cooled catalyst is introduced into the bottom of the reaction zone and hot catalyst is withdrawn from the top of the zone, it is obvious that there is a thermal gradient along the height of the reactor. The adverse efiect of a varying reaction temperature on the attainment of a desired product distribution has been previously mentioned.

A principal object of my invention is to provide a commercially attractive synthesis process in which the best features of fluidization and of a tubular reaction zone immersed in coolant are incorporated without entailing the usual attendant disadvantages.

Another important object is to provide a compact reactor in which the reaction zone is in tubular form and is maintained within very close limits at any desired reaction temperature.

A further object is to avoid the extensive installation of auxiliary equipment, such as cyclone separators, hoppers and the like, conventionally associated with gas-phase reactions involving powdered catalysts.

Still another object is to provide a method which ensures proper fluidization in each and all of several tubes which together form a reaction zone.

Other objects of my invention will be apparent in the description which follows.

In accordance with my invention, synthesis gas, i. e., carbon monoxide and hydrogen, is distributed to and passed up through, a multiplicity of tubular reaction zones which become one at their upper and lower ends. A suitable catalyst, e. g., powdered iron, in fluidized condition fills the tubular reaction zones as well as the merging zones at the upper and lower ends of the tubular zones, The tubular zones are surrounded with a coolant, such as water, Dowtherm or mercury, so that they can be maintained very closely to the desired reaction temperature. It is critical that the tubular zones, which in section may be elliptical, square or polygonal as well as circular, have an effective size of a pipe having an internal radius of not less than about inch and not more than about 4 inches. By efiective pipe size I mean that in any tubular zone the farthest catalyst particle shall be not less than about /5 inch and not more than about 4- inches away from the closest wall of the tubular zone. Preferably, the effective pipe size of my tubular reaction zones is not less than about 1 inch and not more than about 2 inches in internal radius. The tubular zone may be annular in section and, in such case, assuming that the inner surface of the annulus is a cooling surface, one-half of the width of the annulus is "equivalent to the internal radius of a pipe. A relatively inert gas, e. g., hydrogen or a mixture of methane, ethane, etc., is introduced into the bottom zone so as to maintain the powdered catalyst therein in a fluidized state and to facilitate the flow of catalyst up into the tubular reaction zones as needed; the inert fluidizing gas also flows up the reaction tubes, mingling with the reaction gases. The combined gases discharge from the multiple reaction tubes into the-top zone which is of larger horizontal crosssection than the sum of the cross-sections of the reaction tubes. Accordingly, the gases undergo a decrease in velocity so that a denser fluidized mass of catalyst is established in the upper zone in which the reaction tubes merge. Also, because of decreased velocity, the reaction gases which become disengaged from the bulk of the powdered catalyst in the upper zone and flow out of the reactor carry relatively little quantity of catalyst. While the fluidization art indicates that gas velocities over a wide range may be employed, I find it advisable with tubes of the size specified herein to keep the linear velocity or the gases within the range of about 0.1 to about 2.5 feet per second. My preferred range embraces gas velocities of about 0.5 to about 1.5 Ieetper second. In the upper and lower merging zones the gas velocity may be as low as 0.03 foot per second oreven lower.

As mentioned hereinbefore, the size of the reaction tubes is critical to the operability and a success of my process. From heat transfer con- 'siderations, smaller and smaller reaction tubes are desired to provide adequate cooling surface, but from the point of view of good fluidization larger and larger tubes are desired to minimize interfering wall efiects. In reconciling these opposing factors I have determined that my tubular reaction zones must have an efie'ctive pipe size of about 4 inch to about 4 inches in internal radius. Those skilled in the practice of fluidization will appreciate the difliculties of maintaining a satisfactorily fluidized mass of 'pulverulent catalyst within each and every reaction tube of such small size when holding to gas velocities within the range specified hereinabove; "for example, slight surges in the feeding of gases to the reaction tubes will tend to blow the catalyst out of one or more of the tubes. By my invention, such difficulties are largely overcome or their adverse effect is very considerably minir'nized inasmuch as proper fluidization is almost immediately reestablished the moment that any interruption occurs. For such reasons, I maintain a relatively dense mass of fluidized catalyst inthe upper zone to act as a stabilizing cap on 4 the fluidized catalyst mass within the reaction tubes. The mass of fluidized catalyst; in the bottom zone of my reactor acts as an emergency reservoir to supply catalyst promptly to any reaction tube from which part or all of its catalyst charge may have been transported into the upper zone of the reactor. To ensure further the attainment of good fluidization within the small reaction tubes, I prefer to have a standpipe or equivalent connection between the upper and lower zones, filled with fluidized catalyst, so as to permit the immediate flow of catalyst, which may be carried up out of the reaction tubes, to the lower zone whence the catalyst surges up into any reaction tubesdeficient in catalyst content. The automatic and rapid replenishment of catalyst in the reaction tubes is conveniently achieved by a difference in the densities "of the fluidized mass within the standpipe and the reaction tubes. A greater density in the standpipe exerts a pressure on the catalyst mass comparable to a hydrostatic head in a liquid system; this pressure causes the powdered catalyst in the lower zone to rise into the reaction tubes. While for the sake of elucidation I have set forth the foregoing theory of operation to explain the phenomena that occur in, and make possible, the operation of my process which is dependent upon the maintenance of good fluidization in relatively small tubes, I do not wish to be held thereto; it sumces to have an apparatus with the necessary and cooperating elements and to use such apparatus under the conditions brought out in this specification.

The invention will be more clearly and readily understood by reference to the accompanying drawing in which:

Figure 1 is a schematic representation in vertical section of one form of tubular reactor of my invention;

Figure 2 is a similar view of another form of tubular reactor and Figure 3 is a vertical section of a modified reaction tube which may be embodied in the reactors of my invention.

' The same numerals are used to'indicate similar or equivalent elements in the three figures.

The reactors have a main reaction shell I preferably circular in horizontal cross-section, a bottom tube sheet 2 and a top tube sheet t'which hold a multiplicity of reaction tubes 4'. A standpipe 5 is shown in Figure 1 at the center of the bundle of reaction tubes '4 and in Figure 2 the standpipe is the annular space between the large tube or shell 5 and the reactor shell 1. In Figure 2, brackets 5a support shell 5 which encloses the bundle of tubes 4, by attachment to the main; reactor shell I. An inlet 6 serves to introduce a coolant into the zone surrounding the reaction tubes 4, while outlet '1 is for the withdrawal of heated coolant. The reactors have atapered or funnel-shaped bottom section 8 'wi'th a gas inlet d. In Figure 1, standpipe 5 is-represented as having an expanded bottom portion it"; this seems desirable to minimize any tendency of the powdered catalyst to pack within thestandpipe as the catalyst moves down therethrough. A conical plug H projects up into standpipe 5 and, by adjustment of the supporting threaded rod I2, plug H may be movedin or out to give any desired opening 13 at the bottom of standpipe 5. Similarly, in Figure 2 a ring [1' having a wedge-shaped cross-section is made to slide'up or down to control the opening [3 at the bottom of the annular space which is used for'the return of powdered catalyst to the bottom section 8 of the reactor. The position of the ring H is set by adjustment of the threaded rod l2, which through a ball-socket joint and forked rod members lZa supports the ring ll. Pipe M has a ring-shaped portion with several nozzles [4a to distribute a fiuidizing gas within the annular zone outside of shell 5; in Figure 1, pipe I4 is likewise used for the introduction of fiuidizing gas into standpipe 5. Pipes l5 are used for the introduction of synthesis gas. These pipes have several needle-like members IE to feed the synthesis gas up into the reaction tubes 4. The reactors have a top section II with a vent pipe l8 for the withdrawal of the gaseous reaction products. Top section I! may also have an opening or manhole 19 (shown covered up) for ready access into the top of the reactor. Opening l9 may be used for the charging of catalyst powder into the reactor. Similarly, the bottom section 8 may have an opening or manhole 20 (shown covered up) for the withdrawal of catalyst and for access into the bottom of the reactor. It is often found desirable to operate the reactor with a slow but continuous reactivation of the powdered catalyst. In such cases the openings I9 and 20 are connected to suitable piping for the continuous introduction of reactivated catalyst and for the continuous withdrawal of fouled or spent catalyst, respectively.

Figure 3 is a vertical section or a modified reaction tube 4 which has an inner tube 4a with bent portions 41) and openings 40 through the walls of tube 4. By this modification more cooling surface is introduced into reaction tube 4; such modification is particularly desirable with the larger reaction tubes. With this type of tube the reaction zone is annular in horizontal crosssection. The same coolant which surrounds tube 4 flows through tube 40 and accordingly maintains the same temperature on the inner and outer walls of the annular reaction zone.

E have shown the top tube sheet 3 as being conical so as to facilitate the movement of powdered catalyst, that may discharge from the tops of the reaction tubes 4, back to the lower zone of the reactor whence the catalyst is fed up into the reaction tubes. In Figure 1, because of the conical sheet 3, the catalyst rising into the top zone of the reactor migrates more readily into the central standpipe 5, while in Figure 2 the inverted cone promotes the movement of catalyst discharging from the reaction tubes to the annular zone between shells 5 and l. A fiat tube sheet may be used at the top of the bundle of reaction tubes since the maintenance of an appreciable depth, say about 1 toot, of fluidized catalyst above the tube sheet will facilitate the movement of catalyst particles in horizontal directions.

Having described typical reactors of my invention as Well as their operation, I shall cite the details of a synthesis plant producing 100 barrels per day of liquid hydrocarbons. The reactor is of the type shown in Figure 1; it has 300 reaction tubes made from steel tub-ing of 3-inch outside diameter -inch wall thickness) and a central standpi-pe having a 16-inch outside diameter. The 300 reaction tubes are distributed around the standpipe with clearances of about 1 inch between adjacent tubes. While the length of the reaction tubes varies somewhat because of the conical tube sheet at the top of the tube bundle, the average length of the tubes is 15 feet. The coolant surrounding the reaction tubes is water; the reactor therefore functions like a steam boiler in which the heat is supplied by conducting hot T particles are well distributed over a. fairly broad There is suificient fluidized catalyst in range. the reactor to fill the reaction tubes, the standpipe, and the upper and lower merging zones. The fluidized mass of catalyst has a pseudo-liquid level, i. e., the level at which the bulk of the re-- action gases become disengaged from the fluid mass, which is about 1 foot above the upper en of the longest reaction tubes.

Fresh synthesis gas containing 1.2 to 1.3 volumes of hydrogen for each volume of carbon. monoxide and minor proportions of carbon di-' oxide, water and nitrogen is introduced into the reactor at the rate of 510 pound-mols per hour.

This synthesis gas with an average molecular weight of 15 is distributed and fed into the 300 reaction tubes. At the same time, 316 poundmols of recycle gas flows through the reactor, about of this gas entering through the lower conical section, thereby maintaining fiuidiz-ationin the lower zone and making catalyst powder available for transport into any reaction tubes which may become deficient in catalyst content, and about 10% of the gas entering at the bottom of the standpipe to keep the catalyst therein in a fluid condition. The recycle gas which is the gas remaining after all the liquid products have been recovered from the eflluent gases of the reactor is composed largely of carbon dioxide, hydrogen and gaseous hydrocarbons like methane, ethane and ethylene. The average molecular weight of recycle gas is 24. The 90% of recycle gas entering at the bottom of the reactor becomes distributed and flows through the 300 reaction tubes along with the fresh synthesis gas fed to each tube. The combined gases pass up through the reaction tubes with a linear velocity in the vicinity of- 1 foot per second and satisfactory fluidization of the catalyst powder results. The reaction zone is under a pressure of 250 pounds age.

With these conditions, barrels (42 gallons per :barrel) of liquid hydrocarbons are produced daily. The liquid product comprises about 80% of hydrocarbons boiling in the gasoline range, i. e., a. fraction starting with hydrocarbons of four carbon atoms and ending at a boiling point of 400 F., and about 20% 0a: hydrocarbons boiling above 400 F. I

With the selected operating variables, the process not only yields valuable liquid hydrocarbons but also .the operation is continuous and free of interruptive difficulties. Thus, because of satisfactory fiuidization of the powdered catalyst within the reaction tubes and because of the extensive cooling surface of the reaction tubes, the entire reaction mass is maintained at the chosen temperature of 600 F. in spite of the great exo'- thermicity of the hydrogenation of carbon monoxide. As previously pointed out, any tendency of the catalyst to bewblown out of any reaction tube is immediately nullified by the reservoir of eata-- The x ly'st in the upper and lower zones of the reactor and the standpipe' connecting these zones.

The combination of these zone and standpipe isanalo'gous to an elevated water tank; the fluid is always ready to flow. In the fluid reactor of this invention, the moment any reaction tube is emptied of its catalyst charge, another charge of catalyst surges into it. The advantages of such continuous and steady operation are high yields of synthetic products, a favorable product distribution, and a long active life for the catalyst. The long catalyst life may be attributed to two factors: the closetempera'ture control in my reactor prevents thermal injury of the catalyst resulting-from sudden temperature surges and the passage of relatively nonreactive recycle gas up through the catalyst mass in the standpipe tends to volatilize or strip absorbed heavy hydrocarbone from the catalyst as it moves downwardly incountercurrent relation to the recycle gas. Because of the generally uniform condition of fluidity and turbulence of the catalyst mass in the several. tubes, goodheat transfer from the catalyst "to the tube walls is established and fluctuations in reaction temperature are held within limits ofas low as to :10 IF;

A distinct advantage or my invention over prior processes using .finelydivid'ed catalysts resides in thefa'ct that relatively small quantities of catalyst particles leave-the reactor. Prior processes have been predicatedonhigh rates of introduction and withdrawal of the catalyst in the reactor; such operation has necessitated elaborate systems for theseparation of the powdered-catalyst from the enluent reaction gases. systems, becauseof the heavy duty to which they are exposed, are large and expensive both in first cost and upkeep. In my process, a relatively dense phase of powdered catalyst in the upper zone of the reactor blankets the upper ends of the reaction tubes from which powder would otherwise be 'transported'at'an appreciable rate. small quantity of powder which may leave the reactor by entrainment in the eliluent gases is readily recovered by a suitable, small separator, e. g, a-cyclone, bag filter, or the like. The recovered catalyst-may be returned to the reactor by any of several known procedures, such as suspension in the recycle-gases entering at the bottom of the reactor- The catalyst employed in my process is an essential contributing factor for commercial operability. From this viewpoint, I prefer to use iron catalyst although catalysts of the other metals of the irongroup, viz., cobalt and nickel, arewell suited to my process and, in certain instances, may o-fie-r some advantages over iron. The catalyst is predominantly, i.e., at least 80% a metal or a mixture of metals of the iron group. I am, of course, aware that various promoters and activators may be added to the iron group metals in minor proportions, i. e., not more than to modify the hydrocarbon synthesis reaction and thereby to yield different hydrocarbon products. Such promoters as compounds of alkali and-alkaline earth metals, the oxides of titanium and silicon, and salts of molybdenum and chro mi-um may be employed. Inasmuch as both components of synthesis gas, via, hydrogen and carbon monoxide, are strong reducing agents, the powdered catalyst charged to the reactor may be in the formof any readily reducible compound or compounds of metals of the iron group.

While relatively line or relatively coarse cata lyst powders may be used, I generally choose These catalyst recovery powdersotE-about 260* to coo mesh. Such powders preferably have apredominant-fraction, say passing through a 3-2 -mesh screen and the particle'sizes in this fraction are distributed over a fairly broad range. Instead of pulverizing the catalyst itself, thecatalytic material may be deposited by known technique on finely divided, inert supports like diatomaceous earth. Accordingly, powdered catalysts suitable for my fluid synthesis process embrace both the unsupported andthe 7 supported types.

It understood that the selection of the several process variables, such as temperature, pressure ratio of carbon monoxide to hydrogen in the feedtgas, catalystcomposition,-etc., depend largely onthe products desired. There are extensive teachings in the technicalliterature which relate to the variables of the synthesis reaction and to their influence on the products obtained.

To recapitulate, my invention involves asynthcsis process which employs powdered catalyst in a, multiplicity of relatively small reaction tubes surrounded by a suitable coolant. The reactor with multiple tubes is of'novcl design and includes an upper-and a lower zone which communicate with-the respectiveends of the reaction tubes and which are connected toeach'other through a vertical zone or passageway, viz., the standpipe of Figure lor theannular space of Figure 2. The tubes, the upper and lower zones and the connecting passageway are filled with fluidized catal st, the fluidized mass being of higher density in the upper and lower zones and the connecting passageway thanin the reaction tubes. This difference in density promotes, so to speak, the migration of powdered catalyst from these zones to the tubes and thus ensures that the tubes are at-all times properly charged with fluidized catalyst. Inasmuch as the synthesis gas is admitted to, and flows through, the reaction tubes only in proximity of cooling walls, very sensitive thermal regulation is achieved.

It is clear that the apparatus of my invention is applicable more broadly to any chemical reaction between finely divided solids and vapors or gases, which involves a large quantity of reaction energy, whether exothermic or endothermic. 'In an endothermic reaction, a heating fluid instead of a coolant-is circulated in contact with. the exterior walls of the reaction tubes. In either case, the same accurate control of the reaction temperature is accomplished by a reactor which is largely automatic and foolproof in its functioning.

Those skilled in the art will appreciate that the process and apparatus of my invention willpermit of many modifications. For example, it is not necessary to have a relatively large standplpe connecting the upper and lower zones of my reactor; instead, some of the several reaction tubes may be fed with gas at a lower velocity than that used in the other tubes so as to favor the migration of catalyst down through the tubes with lower gas velocity and upthrough the tubes with higher gas velocity. Similarly, the lowerzone of the reactor may be fluidized by the intro'- duction of a gas other than recycle gas, 1. e., the residual fixed gases resulting from the synthesis reaction. Suitable gases include carbon dioxide, methane and hydrogen. Furthermore, recycle gas may be advantageously replaced by avaporizable liquid. Such a liquid, e. g., the fraction of the synthesis products which boil at temperatures in the range of 300 to 500 F., would upon introduction into the bottom of the reactor be completely vaporized and the resultant vapors 9 would fluidize the powdered catalyst. The use of liquid has the added feature that the heat of vaporization is abstracted from the hot catalyst so that partial cooling is effected and the cooling load or service of the walls of the reaction tubes is diminished correspondingly. Also, as is known in the art, synthesis conditions may be selected for the production of oxygenated organic compounds such as alcohols.

In view of the many possible modifications within the spirit of my invention, the claims which follow should be construed broadly and not in a restricted sense based on the illustrative embodiments presented herein.

What I claim is:

1. An apparatus for conducting exothermic and endothermic reactions involving gaseous reactants and finely divided, fluidized, solid particles, comprising an upstanding vessel; a heat exchanger positioned in said vessel having a pair of transverse tube sheets vertically spaced from each other and from the upper and lower extremities of said vessel to form within said vessel an upper chamber above the upper tube sheet and a lower chamber below the lower tube sheet, a multiplicity of vertical tubes extending between said tube sheets and communicating at their extremities, respectively, with said upper and lower chambers, and means for feeding into and withdrawing from the space about said tubes and between said tube sheets a heat transfer medium; gas inlet and outlet means communicating, respectively, with said lower and upper chambers; a passageway substantially larger in cross section than the pipe size of said tubes and connecting said lower and upper chambers, the upper tube sheet being in the form of a conical surface slopin downwardly toward the upper end of said passageway; and a distributor positioned within said lower chamber for injecting a fluid individually into the lower ends of said tubes.

2. The apparatus according to claim 1, wherein the upper tube sheet slopes downwardly toward its center and connects with the upper end of said passageway.

3. The apparatus according to claim 1, wherein the upper tube sheet slopes downwardly toward its perimeter and connects with the upper end of said passageway.

4. The apparatus according to claim 1, wherein said tubes have an effective pipe size of not less than about inch and not more than about 4 inches internal radius.

5. The apparatus according to claim 1, wherein said tubes have an effective pipe size of not less than about 1 inch and not more than about 2 inches internal radius.

6. The process of manufacturing hydrocarbons from a synthesis gas mixture containing carbon monoxide and hydrogen wherein a finely divided synthesis catalyst is contacted with the synthesis gas mixture while in fluidized state, said process being carried out in a closed process zone containing an upper catalyst zone, an intermediate cooling zone comprisin a group of vertical reaction tubes, a lower catalyst zone, a catalyst reactivation zone disposed centrally of, surrounded by, and communicating with said reaction tubes, and comprising a conduit leading from said upper zone to said lower zone and passing centrally through said cooling zone, said process comprising maintaining in said upper zone a suspension of the synthesis catalyst in reaction gas in dense fluidized state, continuously passing the synthesis catalyst in fluidized condition from said upper zone to said reactivation zone, removing high molecular weight reaction products from the catalyst particles in said reactivation zone by contacting the synthesis catalyst with a gas rich in hydrogen, withdrawing the synthesis catalyst in a fluidized condition from the reactivation zone downwardly through said conduit to said lower zone, feeding said synthesis gas into admixture with the catalyst from said lower zone at the lower portion of said reaction tubes to form a dilute mixture of synthesis catalyst therein and then passing said dilute mixture upwardly through said cooling zone in a plurality of confined streams in said tubes under synthesis conditions of temperature and pressure into the bottom of said upper catalyst zone to form the dense fluidized bed of synthesis catalyst in said upper zone.

7. The process of manufacturing hydrocarbons from a synthesis gas mixture containing carbon monoxide and hydrogen wherein a finely divided synthesis catalyst is contacted with the synthesis gas mixture while in fluidized state, said process being carried out in a closed process zone containing an upper catalyst zone, an intermediate cooling zone comprising a group of vertical reaction tubes, a lower catalyst zone, a catalyst reactivation zone disposed centrally of, surrounded by, and communicatin with said reaction tubes, and comprising a conduit leading from said upper zone to said lower zone and passing centrally through said cooling zone, said process comprising maintaining in said upper zone a suspension of the synthesis catalyst in reaction gas in dense fluidized state, continuously passing the synthesis catalyst in fluidized condition from said upper zone to said reactivation zone, removing high molecular weight reaction products from the catalyst particles in said reactivation zone by contacting the synthesis catalyst with a gas rich in hydrogen, withdrawing the synthesis catalyst in a fluidized condition from the reactivation zone downwardly through said conduit to said lower zone, feeding said synthesis gas into admixture with the catalyst from said lower zone at the lower portion of said reaction tubes to form a dilute mixture of synthesis catalyst therein and then passing said dilute mixture upwardly through said cooling zone in a plurality of confined streams in said tubes under synthesis conditions of temperature and pressure into the bottom of said upper catalyst zone to form the dense fluidized bed of synthesis catalyst in said upper zone and continuously causing the synthesis catalyst, in fluidized condition, to rise into said cooling zone from said lower zone.

PERCIVAL C. KEITH.

REFERENCES CITED The following references are of record in the file of this patent:

UNITED STATES PATENTS Number Name Date 468,776 Morrell Feb. 8, 1892 1,466,357 Engel, Sr Aug. 28, 1923 1,967,837 Naab July 24, 1934 2,347,682 Gunness May 2, 1944 OTHER REFERENCES Badger et al., Elements of Chemical Engineering, 1936, pp. 179-81. 

6. THE PROCESS OF MANUFACTURING HYDROCARBONS FROM A SYNTHESIS GAS MIXTURE CONTAINING CARBONS MONOXIDE AND HYDROGEN WHEREIN A FINELY DIVIDED SYNTHESIS CATALYST IS CONTACTED WITH THE SYNTHESIS GAS MIXTURE WHILE IN FLUIDIZED STATE, SAID PROCESS BEING CARRIED OUT IN A CLOSED PROCESS ZONE CONTAINING AN UPPER CATALYST ZONE, AN INTERMEDIATE COOLING ZONE COMPRISING A GROUP OF VERTICAL REACTION TUBES, A LOWER CATALYST ZONE, A CATALYST REACTIVATION ZONE DISPOSED CENTRALLY OF, SURROUNDED BY, AND COMMUNICATING WITH SAID REACTION TUBES, AND COMPRISING A CONDUIT LEADING FROM SAID UPPER ZONE TO SAID LOWER ZONE AND PASSING CENTRALLY THROUGH SAID COOLING ZONE, SAID PROCESS COMPRISING MAINTAINING IN SAID UPPER ZONE A SUSPENSION OF THE SYNTHESIS CATALYST IN REACTION GAS IN DENSE FLUIDIZED STATE, CONTINUOUSLY PASSING THE SYNTHESIS CATALYST IN FLUIDIZED CONDITION FROM SAID UPPER ZONE TO SAID REACTIVATION ZONE, REMOVING HIGH MOLECULAR WEIGHT REACTION PRODUCTS FROM THE CATALYST PARTICLES IN SAID REACTIVATION ZONE BY CONTACTING THE SYNTHESIS CATALYST WITH A GAS RICH IN HYDROGEN, WITHDRAWING THE SYNTHESIS CATALYST IN A FLUIDZED CONDITION FROM THE REACTIVATION ZONE DOWNWARDLY THROUGH SAID CONDUIT TO SAID LOWER ZONE, FEEDING SAID SYNTHESIS GAS INTO ADMIXTURE WITH THE CATALYST FROM SAID LOWER ZONE AT THE LOWER PORTION OF SAID REACTION TUBES TO FORM A DILUTE MIXTURE OF SYNTHESIS CATALYST THEREIN AND THEN PASSING SAID DILUTE MIXTURE UPWARDLY THROUGH SAID COOLING ZONE IN A PLURALITY OF CONFINED STREAMS IN SAID TUBES UNDER SYNTHESIS CONDITIONS OF TEMPERATURE AND PRESSURE INTO THE BOTTOM OF SAID UPPER CATALYST ZONE TO FORM THE DENSE FLUDIZED BED OF SYNTHESIS CATALYST IN SAID UPPER ZONE. 